the evolution of texture was discussed during the formation of ultra-fine and nano grains in a magnesium alloy severely deformed through accumulative back extrusion (abe). the microstructure and texture obtained after applying multiple deformation passes at temperatures of 100 and 250°c were characterized. the results showed that after single abe pass at 100°c an ultrafine/nano grained microstr...

a review on the microstructural evolution in magnesium alloys during severe plastic deformation waspresented. the challenges deserved to achieve ultrafine/ nanostructured magnesium were discussed.the characteristics of the processed materials are influenced by three main factors, including i)difficult processing at low temperatures, ii) high temperature processing and the occurrence ofdynamic r...

An AM30 magnesium alloy was processed through ECAP method at 200 °C. Optical and transmission electron microscopy as well as electron back scattered diffraction (EBSD) technique were employed to characterize the deformed microstructure. A partially recrystallized microstructure including ultrafine/nano structures was obtained. The area fraction of 49% was measured for the recrystallized regions...

Uniform and single-crystalline Mn(3)O(4) nano-octahedrons have been successfully synthesized by a simple ethylenediaminetetraacetic acid disodium salt (EDTA-2Na) assisted hydrothermal route. The octahedron structures exhibit a high geometric symmetry with smooth surfaces and the mean side length of square base of octahedrons is ∼160 nm. The structure is reckoned to provide superior functional p...

Starting from Ni-Co-Mn carbonate nanoparticles prepared by microreaction technology, uniform spherical particles of Ni1/3Co1/3Mn1/3CO3 with a size of 3–4 μm were obtained by a controllable hydrothermal conversion with the addition of (NH4)2CO3. Based on characterizations on the evolution of morphology and composition with hydrothermal treatment time, we clarified the mechanism of this novel met...

High-frequency impacting and rolling was applied on AZ31B magnesium alloy to obtain a gradient nano-structured surface. Surface characteristics were experimentally investigated, and the nanocrystallization mechanism is discussed in detail. Results showed that the gradient nano-structure with the characteristics of work hardening, compressive residual stress and a smooth surface was induced on t...

The evolution of texture was discussed during the formation of ultra-fine and nano grains in a magnesium alloy severely deformed through accumulative back extrusion (ABE). The microstructure and texture obtained after applying multiple deformation passes at temperatures of 100 and 250°C were characterized. The results showed that after single ABE pass at 100°C an ultrafine/nano grained microstr...

Abstract Nano-Al 2 O 3 dispersion-strengthened Cu20W composite was fabricated by vacuum hot-pressing sintering process. The electrical conductivity, relative density, and Brinell hardness were tested, respectively. gleeble-1500D thermomechanical simulator used to conduct isothermal compression with strain rates ranging from 0.001 10 s −1 the temperatures 650 950°C. microstructure of Cu–Al /20W ...

An ultrafine/nano grained AZ31 magnesium alloy was produced through four-pass ECAP processing. TEM microscopy indicated that recrystallized regions included nano grains of 75 nm. Pole figures showed that a fiber basal texture with two-pole peaks was developed after four passes, where a basal pole peak lies parallel to the extrusion direction (ED) and the other ~20° away from the transverse dire...